How to Improve the Adhesion of Neoprene Glue to Glass Fiber Cloth?

Views : 654
Author : Heaterk
Update time : 2022-07-28 16:05:05

Neoprene-coated fiberglass fabric is a commonly used coating composite material in the industry. This material has excellent high and low-temperature resistance and is waterproof, oil-proof, ozone-resistant, and anti-aging, so it is widely used in various industries.

Then in the production process of neoprene, the adhesion of the butadiene rubber glue to the glass fiber cloth significantly influences the product's quality. Heaterk provides some suggestions based on years of manufacturing experience; hoping to help you.

Neoprene coating process

The peel strength of the neoprene adhesive is related to the formula, process, and usage. The available neoprene adhesive needs to add tert-butyl phenolic resin to improve the adhesion to complex and dense adherents such as metal, glass, thermosetting plastics, etc. As the amount of resin increases, the peel strength increases, but when the amount of resin exceeds 45 parts (CR is 100 parts), the peel strength decreases instead. Therefore, too small or too little amount of 2402 resin will make the peel strength lower.

After the chloroprene rubber is mixed, the relative molecular weight is reduced, the viscosity of the glue is small, and the wettability is good, which can improve the peel strength.

When the neoprene adhesive is used to bond non-porous adherents, the drying time after gluing should not be too short. Otherwise, the solvent will be wrapped after lamination, and the peel strength will be reduced. In addition, it should be compacted and smashed after lamination to drive out the air. Otherwise, the peel strength will be reduced. The outstanding feature of neoprene adhesive is the high initial strength, but it takes 5~7 days to reach the maximum power. Allow enough time for actual use and evaluation of management.

In short, to increase the peel strength of the neoprene adhesive, a certain amount of 2402 resin should be added. It is appropriate to use 40~50 parts. The neoprene rubber should be adequately mixed to make the glue have good wettability. 100 parts of hydroxyl CRAF, 45 pieces of tert-butyl phenolic resin, five pieces of light magnesium oxide, 165 pieces of toluene, acetic acid Neoprene adhesive prepared with 165 pieces of ethyl ester and 165 parts of n-hexane, its peel strength is 1.15K.m-1

Get in touch with the experts at Heaterk to discuss more expertise in coated fiberglass fabrics


Related News
What Is Thermal Insulation? What Is Thermal Insulation?
Oct .31.2023
Discover the importance of thermal insulation in energy efficiency and comfort. Delve into materials, applications, and data-driven insights in this comprehensive guide.
What Are the Benefits of Insulating Coatings? What Are the Benefits of Insulating Coatings?
Oct .31.2023
Uncover the benefits of insulating coatings, including improved thermal insulation, reduced heat transfer, corrosion protection, and energy efficiency. Find out how these coatings can lower energy costs and minimize environmental impact.
What is fire resistant fabric made of? What is fire resistant fabric made of?
Oct .30.2023
Fire-resistant fabric, with its unique fiber blend, offers unmatched fire resistance. Its key? A special retardant properties woven into every strand.
What Is Important For Insulation? What Is Important For Insulation?
Aug .08.2023
Delve into the integral role of insulation in maintaining home comfort, improving energy efficiency, and contributing to sustainability. Discover the various types of insulation, including Heaterk's specialty products. Understand how insulation works to reduce heat flow, when to consider insulation upgrades, and the impact of insulation on energy costs and carbon emissions.